Phase Stability of Rapidly Solidified (Fe1−xNix)88Zr7B4Cu1 Ribbons

Arvindha Babu, D. and Majumdar, Bhaskar and Sarkar, R. and Murty, B S (2021) Phase Stability of Rapidly Solidified (Fe1−xNix)88Zr7B4Cu1 Ribbons. Metallurgical and Materials Transactions A, 52 (2). pp. 560-573. ISSN 1073-5623

Full text not available from this repository. (Request a copy)

Abstract

In this study, the glass-forming ability (GFA), structure and microstructure of (Fe1−xNix)88Zr7B4Cu1 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8 and 1.0) alloys, in both the as-melt spun and heat-treated conditions, have been investigated. Almost complete amorphization was observed only for x = 0, 0.4 and 0.5 alloys at the highest melt spun wheel speed of 47 m/s. At lower wheel speeds all alloys are partially crystalline. The crystalline phases are bcc solid solution (bcc-SS) up to a composition of x = 0.2 and fcc solid solution (fcc-SS) for x = 0.6 and above. At a melt spun wheel speed of 47 m/s, the alloy with the composition of x = 0.3 is almost amorphous, along with traces of both bcc and fcc phases. Ribbons annealed at 450 °C/500 °C (after the first exothermic peak observed in DSC result) exhibit bcc-SS at low Ni concentration (up to x = 0.4) and fcc-SS at higher Ni concentration (x = 0.6 and beyond), whereas x = 0.5 ribbon shows the formation of both bcc-SS and fcc-SS. Ribbons annealed at 620 °C/750 °C (after the second exothermic peak observed in DSC results) exhibit Fe3Zr at low Ni concentration up to x = 0.3 and Ni5Zr from x = 0.4. The crystalline phases form during melt spinning are in the form of dendrites of submicron size, whereas the precipitated phases formed during annealing are nanocrystalline in nature. Thermodynamic modeling was carried out to understand the GFA and phase formation, which are in conformity with the experimental observations. © 2021, The Minerals, Metals & Materials Society and ASM International.

[error in script]

IITH Creators:

IITH Creators	ORCiD
Murty, B S	https://orcid.org/0000-0002-4399-8531

Item Type:

Article

Additional Information:

This work was supported by Defence Research and Development Organization (DRDO), New Delhi, India. The authors thank Dr. RP Mathur, Group Head, Advanced Magnetics Group, DMRL, and Dr. G Madhusudhan Reddy, Director, DMRL, for continued support and permission to publish this work.

Uncontrolled Keywords:

BCC solid solution; Crystalline phasis; Glass-forming ability; Heat treated condition; Partially crystalline; Rapidly solidified; Structure and microstructures; Thermodynamic model

Subjects:

Materials Engineering > Materials engineering

Divisions:

Department of Material Science Engineering

Depositing User:

. LibTrainee 2021

Date Deposited:

13 Sep 2022 08:45

Last Modified:

13 Sep 2022 08:45

URI:

http://raiithold.iith.ac.in/id/eprint/10558