Nearly full-density pressureless sintering of AlCoCrFeNi-based high-entropy alloy powders

Rohila, Sahil and Mane, Rahul B and Ummethala, Govind and Panigrahi, Bharat Bhooshan (2019) Nearly full-density pressureless sintering of AlCoCrFeNi-based high-entropy alloy powders. Journal of Materials Research. pp. 1-10. ISSN 0884-2914

Full text not available from this repository. (Request a copy)

Abstract

AlCoCrFeNi is among the promising high-entropy alloys (HEAs) that possess high strength with considerable ductility. Powder sintering is one of the competitive routes for the production of HEA powders. However, sintering of HEA powders under a pressureless condition is difficult. The present work aims to produce high-density components from mechanically alloyed AlCoCrFeNi HEA powders through the pressureless sintering method. Nearly full density was achieved at 1275 °C. Sintering was performed in the presence of a viscous phase in the temperature range of 1200–1250 °C, which was confirmed through differential scanning calorimetry and dilatometric measurements. This viscous phase was found have a Cr-rich composition, detected by interrupting the sintering and quenching of the sample. The powder initially contained the BCC phase with a small fraction of FCC and other phases. During sintering, a significant fraction of the FCC phase and nanosized B2 phase were formed. Sintered sample had a hardness of 679 ± 20 Hv.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Panigrahi, Bharat BhooshanUNSPECIFIED
Item Type: Article
Uncontrolled Keywords: sintering, mechanical alloying, powder metallurgy
Subjects: Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: Team Library
Date Deposited: 26 Feb 2019 09:14
Last Modified: 26 Feb 2019 09:14
URI: http://raiithold.iith.ac.in/id/eprint/4842
Publisher URL: http://doi.org/10.1557/jmr.2019.9
OA policy: http://www.sherpa.ac.uk/romeo/issn/0884-2914/
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 4842 Statistics for this ePrint Item