Mechanical activated synthesis of alumina dispersed FeNiCoCrAlMn high entropy alloy

Prasad, H and Singh, S and Panigrahi, Bharat Bhooshan (2017) Mechanical activated synthesis of alumina dispersed FeNiCoCrAlMn high entropy alloy. Journal of Alloys and Compounds, 692. pp. 720-726. ISSN 0925-8388

Full text not available from this repository. (Request a copy)

Abstract

The present research aims to investigate the effect of oxide dispersion on the synthesis of High-Entropy (HE) alloy and its properties. For this FeNiCoCrAlMn High-Entropy (HE) alloy dispersed with 2 wt percentage alumina (Al2O3) was synthesized by mechanical activated synthesis. The mechanical activation was carried out by milling the elemental powder mixture of aluminum, cobalt, chromium, iron, nickel and manganese in an equiatomic ratio up to 20 h 2 wt% of Al2O3 was added during mechanical alloying to obtain oxide dispersed HE alloy. Upon pyrolysis at high temperature FCC was emerged as major phase in both alloys (with and without oxide dispersion). The alumina dispersed HE alloy shows increase in size of AlNi and CrFeMn rich phase after sintering, relatively less thermal expansion coefficient and better oxidation resistance than HE alloy without oxide dispersion. Hardness was found to be doubled after adding 2% alumina. The obtained result indicate that oxide dispersed HE alloy can be useful material for high temperature coating application.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Panigrahi, Bharat BhooshanUNSPECIFIED
Item Type: Article
Uncontrolled Keywords: High-entropy alloy; Mechanical activation; Differential scanning calorimetry; Oxide dispersion; Thermal expansion
Subjects: Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: Team Library
Date Deposited: 14 Sep 2016 06:22
Last Modified: 10 Nov 2017 06:26
URI: http://raiithold.iith.ac.in/id/eprint/2749
Publisher URL: https://doi.org/10.1016/j.jallcom.2016.09.080
OA policy: http://www.sherpa.ac.uk/romeo/issn/0925-8388/
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 2749 Statistics for this ePrint Item