Effect of cold-rolling strain on the evolution of annealing texture of equiatomic CoCrFeMnNi high entropy alloy

Sathiaraj, G D and Bhattacharjee, Pinaki Prasad (2015) Effect of cold-rolling strain on the evolution of annealing texture of equiatomic CoCrFeMnNi high entropy alloy. Materials Characterization, 109. pp. 189-197. ISSN 1044-5803

Full text not available from this repository. (Request a copy)

Abstract

The effect of cold-rolling strain on the evolution of microstructure and texture during annealing was studied in an equiatomic CoCrFeMnNi high entropy alloy. For this purpose the alloy was cold-rolled to 60%, 80% and 95% reduction in thickness. The three cold-rolled materials were isochronally annealed for 1 h at temperatures ranging between 700 °C and 1200 °C. With increasing rolling reduction, the texture transition from pure metal type (< 60% reduction) to an alloy type texture (> 80% reduction) was observed. The final recrystallized grain size was found to decrease systematically with increasing prior cold-rolling strain. However, the effect was much less pronounced below the annealing temperature of 1200 °C due to sluggish diffusion in the HEA. The recrystallization texture of different deformed materials showed the presence of similar texture components indicating that prior deformation had only limited effect on the formation of annealing texture. The typical annealing texture components of low SFE materials, such as {236}<385 > or {113}<332 > were not the dominant components. The volume fractions of different texture components also did not reveal significant dependence on the annealing temperature. The evolution of annealing texture in the HEA could be adequately explained by the absence of strong preferential nucleation and growth.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Bhattacharjee, Pinaki Prasadhttp://orcid.org/0000-0002-6422-2601
Item Type: Article
Additional Information: The authors also acknowledge Professor J.W. Yeh, National Tsing Hua University, Taiwan for kindly providing the starting HEA used in the present research work.
Uncontrolled Keywords: High entropy alloys; Cold-rolling; Annealing; Microstructure; Texture; EBSD
Subjects: Others > Metallurgy
Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: Team Library
Date Deposited: 13 Oct 2015 09:26
Last Modified: 31 Aug 2017 06:47
URI: http://raiithold.iith.ac.in/id/eprint/1978
Publisher URL: https://doi.org/10.1016/j.matchar.2015.09.027
OA policy: http://www.sherpa.ac.uk/romeo/issn/1044-5803/
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 1978 Statistics for this ePrint Item