Monoclinic Cc-phase stabilization in magnetically diluted lead free Na1/2Bi1/2TiO3—Evolution of spin glass like behavior with enhanced ferroelectric and dielectric properties

Thangavelu, K and Asthana, Saket (2015) Monoclinic Cc-phase stabilization in magnetically diluted lead free Na1/2Bi1/2TiO3—Evolution of spin glass like behavior with enhanced ferroelectric and dielectric properties. Materials Research Express, 2 (9). 096301. ISSN 2053-1591

Full text not available from this repository. (Request a copy)

Abstract

The effect of magnetic cation substitution on the phase stabilization, ferroelectric, dielectric and magnetic properties of a lead free Na0.5Bi0.5TiO3 (NBT) system prepared by O2 atmosphere solid state sintering were studied extensively. Cobalt (Co) was chosen as the magnetic cation to substitute at the Ti-site of NBT with optimized 2.5 mol%. Rietveld analysis of x-ray diffraction data favours the monoclinic Cc phase stabilization strongly rather than the parent R3c phase. FE-SEM micrograph supports the single phase characteristics without phase segregation at the grain boundaries. The stabilized Cc space group was explained based on the collective local distortion effects due to spin–orbit stabilization at Co3+ and Co2+ functional centres. The phonon mode changes as observed in the TiO6 octahedral modes also support the Cc phase stabilization. The major Co3+-ion presence was revealed from corresponding crystal field transitions observed through solid state diffuse reflectance spectroscopy. The enhanced spontaneous polarization (Ps) from cong38 μC cm−2 to 45 μC cm−2 could be due to the easy rotation of polarization vector along the ${(1\bar{1}0)}_{{\rm{pc}}}$ in Cc phase. An increase in static dielectric response (epsilon) from epsilon cong 42 to 60 along with enhanced diffusivity from γ cong 1.53 to 1.75 was observed. Magneto-thermal irreversibility and their magnetic field dependent ZFC/FC curves suggest the possibility of a spin glass like behaviour below 50 K. The monoclinic Cc phase stabilization as confirmed from structural studies was well correlated with the observed ferroic properties in magnetically diluted NBT.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Asthana, Sakethttp://orcid.org/0000-0002-6420-3304
Item Type: Article
Subjects: Physics
Divisions: Department of Physics
Depositing User: Team Library
Date Deposited: 28 Sep 2015 04:38
Last Modified: 29 Aug 2017 09:40
URI: http://raiithold.iith.ac.in/id/eprint/1953
Publisher URL: https://doi.org/10.1088/2053-1591/2/9/096301
OA policy: http://www.sherpa.ac.uk/romeo/issn/2053-1591/
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 1953 Statistics for this ePrint Item