Synthesis and Sintering Kinetics of Mechanically Alloyed FeCrCoMnNi High Entropy Alloy Powders

Equbal, A (2015) Synthesis and Sintering Kinetics of Mechanically Alloyed FeCrCoMnNi High Entropy Alloy Powders. Masters thesis, Indian Institute of Technology Hyderabad.

[img]
Preview
Text
MS13M1002.pdf - Submitted Version

Download (1MB) | Preview

Abstract

High entropy alloys (HEAs) are solid solution of multi elements system fabricated in equiatomic or near equiatomic composition. These can be fabricated through two processing routes, melting-casting and mechanical alloying (MA). Objectives of this investigation are to synthesize the high purity single phase FeCrCoMnNi HEA powder the mechanical alloying, and to study the sintering kinetics of this alloy powder. Elemental powders of Fe, Cr, Co, Mn and Ni were taken in equi-molar ratio and milled upto 15h using tungsten carbide vials and balls. XRD characterization of milled powders shows that high entropy alloy phase started forming at about 10h of milling; mostly with FCC phase. Milled powders were further characterized using differential scanning calorimetry(DSC) to understand the phase formation behavior during heating. The DSC analysis indicates that the exothermic reactions were occurred at about 470ºC, which may be attributed to the release of internal strains, accumulated during high energy ball milling and release of some dislocations and defects generated during milling. An end of thermic peak at 990ºC, which could be attributed to melting of some intermetallics phases. Post-mechanical alloying annealing treatment upto 1000ºC showed retention of the FCC phases.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Item Type: Thesis (Masters)
Uncontrolled Keywords: High-Entropy Alloys, Mechanical Alloying, Powders, Sintering, Activation Energies; TD362
Subjects: Others > Metallurgy
Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: Library Staff
Date Deposited: 06 Jul 2015 06:07
Last Modified: 16 Jul 2019 05:04
URI: http://raiithold.iith.ac.in/id/eprint/1654
Publisher URL:
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 1654 Statistics for this ePrint Item