Optimizing anion storage performances of graphite/ non-graphitic carbon composites as cathodes for dual-ion batteries

Martha, Surendra Kumar (2023) Optimizing anion storage performances of graphite/ non-graphitic carbon composites as cathodes for dual-ion batteries. Electrochimica Acta, 441. p. 141754. ISSN 0013-4686

Text
eleact_441-141754.pdf - Published Version
Download (6MB)

Abstract

Anion intercalation capacity of graphite cathode is a limiting factor towards the development of dual-ion energy storage devices. A large portion of electrochemically active sites in graphite lattice remains inaccessible to anions due to the instability of electrolytes beyond 5 V. Strategy to composite graphitic intercalation along with surface storage from non-graphitic carbons to enhance capacity is explored in this work. Optimizations are performed to determine the best ratio of graphitic and non-graphitic carbons, and to find out the blend of physical properties of non-graphitic carbons that aid the surface contribution to the greatest extent. Besides, it is also optimized to obtain the maximum achievable lifetime and efficiency, suitable active material loading for balancing energy-power output, and the safest upper cut-off voltage for trading off capacity against cycle life. Surface area, pore size, functional groups, and doped elements govern the electrochemical properties of non-graphitic carbons. A composite of graphite with high surface area carbon (2477 m2 g − 1) in a 75:25 ratio doubles the capacity, whereas the composite of graphite and reduced graphene oxide at the same ratio yields prolonged cycle life at 100 mA g − 1 within 2.0–5.0 V. The capacity improvement is invariably reproducible in dual carbon cell using composite materials as both electrodes.

[error in script]

IITH Creators:

IITH Creators	ORCiD
Martha, Surendra Kumar	https://orcid.org/0000-0002-7762-7237

Item Type:

Article

Uncontrolled Keywords:

Anion intercalation; Carbon composite; Dual-ion cell; Electrochemical optimizations; Graphite cathode; Anion intercalation; Anion storages; Carbon composites; Cycle lives; Dual-ion cell; Electrochemical optimization; Electrochemicals; Graphite cathodes; Non-graphitic carbon; Optimisations; Carbon carbon composites; Cathodes; Graphite electrodes; Negative ions; Pore size; Secondary batteries; Storage (materials); Graphene

Subjects:

Chemistry > Electrochemistry
Chemistry

Divisions:

Department of Chemistry

Depositing User:

Mr Nigam Prasad Bisoyi

Date Deposited:

22 Aug 2023 05:30

Last Modified:

22 Aug 2023 05:30

URI:

http://raiithold.iith.ac.in/id/eprint/11587