Online monitoring of thermo cycles during laser remelting of flame sprayed chromia coating in pulsed mode and coating properties

Das, Biswajit and Gopinath, Muvvala and Nath, Ashish Kumar and et al, . (2021) Online monitoring of thermo cycles during laser remelting of flame sprayed chromia coating in pulsed mode and coating properties. Optik, 227. pp. 1-11. ISSN 0030-4026

[img] Text
Optik.pdf - Published Version
Restricted to Registered users only

Download (6MB) | Request a copy

Abstract

A fiber laser operating in pulsed mode was used to remelt flame sprayed chromia coating. Time-temperature history of laser remelting process was captured using an infrared pyrometer. Temperature of the remelted zone remained steady during remelting. Average temperature increased with an increase in duty cycle and frequency. An improvement in surface roughness was found with an increase in the duty cycle and decrease in frequency. Porosity and inter-lamellar boundary of flame sprayed coating were obliterated upon laser remelting. A columnar grain growth perpendicular to the coating surface was observed. The as-sprayed coating harbored compressive residual stress that decreases with depth. Upon laser remelting, surface residual stress showed a tendency to become tensile. Wear coefficient of the remelted coating 70 % lower than those of the as-sprayed coating. The primary failure modes were splat delamination and radial cracking in as-sprayed and laser remelted coating, respectively. © 2020 Elsevier GmbH

[error in script]
IITH Creators:
IITH CreatorsORCiD
Gopinath, Muvvalahttps://orcid.org/0000-0002-2133-3686
Item Type: Article
Uncontrolled Keywords: Chromia; Mechanical properties; Online monitoring; Pulsed mode laser remelting; Residual stress
Subjects: Physics > Mechanical and aerospace
Divisions: Department of Mechanical & Aerospace Engineering
Depositing User: . LibTrainee 2021
Date Deposited: 12 Sep 2022 09:33
Last Modified: 12 Sep 2022 09:33
URI: http://raiithold.iith.ac.in/id/eprint/10543
Publisher URL: http://doi.org/10.1016/j.ijleo.2020.166030
OA policy: https://v2.sherpa.ac.uk/id/publication/15907
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 10543 Statistics for this ePrint Item